Chemical composition (%) of Stainless Steel Pipes

 
       
   

Grade
AISI

C

Mn

P

S

Si

Cr

Ni

Mo

Other

 J7

 < 0.10

8.50-10.00

< 0.090

< 0.030

< 0.75

15.00-16.00

0.25-0.50

-

-

 J4

 < 0.10

8.50-10.00

< 0.090

< 0.030

< 0.75

15.00-16.00

0.80-1.20

-

-

 201

 < 0.15

5.50-7.50

< 0.060

< 0.030

< 1.00

16.00-18.00

3.50-5.50

-

N < 0.25

 202

 < 0.15

7.50-10.00

< 0.060

< 0.030

< 1.00

17.00-19.00

4.00-6.00

-

N < 0.25

 301

 < 0.15

< 2.00

< 0.045

< 0.030

< 1.00

16.00-8.00

6.00-8.00

-

-

 302

 < 0.15

< 2.00

< 0.045

< 0.030

< 1.00

17.00-19.00

8.00-10.00

-

-

 303

 < 0.15

< 2.00

< 0.20

< 0.15

< 1.00

17.00-19.00

8.00-10.00

< 0.60

-

 303 Se

 < 0.15

< 2.00

< 0.20

< 0.060

< 1.00

17.00-19.00

8.00-10.00

-

Se< 0.15

 304

 < 0.08

< 2.00

< 0.040

< 0.030

< 0.75

18.00-20.00

8.00-11.00

-

-

 304 L

 < 0.035

< 2.00

< 0.040

< 0.030

< 0.75

18.00-20.00

8.00-13.00

-

-

 305

 < 0.12

< 2.00

< 0.045

< 0.030

< 1.00

17.00-19.00

10.50-13.00

-

-

 308

 < 0.08

< 2.00

< 0.045

< 0.030

< 1.00

19.00-21.00

10.00-12.00

-

-

 309

 < 0.25

< 2.00

< 0.045

< 0.030

< 1.00

22.00-24.00

12.00-15.00

-

-

 309 S

 < 0.08

< 2.00

< 0.045

< 0.030

< 1.00

22.00-24.00

12.00-15.00

-

-

 310

 < 0.25

< 2.00

< 0.045

< 0.030

< 0.75

24.00-26.00

19.00-22.00

-

-

 310 S

 < 0.08

< 2.00

< 0.040

< 0.030

< 0.75

24.00-26.00

19.00-22.00

-

-

 314

 < 0.25

< 2.00

< 0.045

< 0.030

1.50-3.00

23.00-26.00

19.00-22.00

-

-

 316

 < 0.08

< 2.00

< 0.040

< 0.030

< 0.75

16.00-18.00

10.00-14.00

2.00-3.00

-

 316 L

 < 0.035

< 2.00

< 0.040

< 0.030

< 0.75

16.00-18.00

10.00-15.00

2.00-3.00

-

 316 Ti

 < 0.08

< 2.00

< 0.045

< 0.030

< 1.00

16.00-18.00

10.00-14.00

2.00-2.50

Ti5*C.Min

 317

 < 0.08

< 2.00

< 0.040

< 0.030

< 0.75

18.00-20.00

11.00-14.00

3.00-4.00

-

 317 L

 < 0.035

< 2.00

< 0.045

< 0.030

< 0.75

18.00-20.00

11.00-15.00

3.00-4.00

-

 321

 < 0.08

< 2.00

< 0.040

< 0.030

< 0.75

17.00-20.00

9.00-13.00

-

Ti < 5xC%

 347  < 0.08 < 2.00 < 0.040 < 0.030 < 1.00 17.00-20.00 9.00-13.00
-
Na+Ta< 10xC%
 409 L  < 0.030 < 1.00 < 0.045 < 0.020 < 1.00 10.50-11.70 < 0.50
-
Ti 6x(C=N)min
 410  < 0.15 < 2.00 < 0.045 < 0.030 < 1.00 11.50-13.50 < 0.75
-
-
 429  < 0.12 < 1.00 < 0.040 < 0.030 < 1.00 14.00-16.00
-
-
-
 430  < 0.12 < 1.00 < 0.040 < 0.030 < 1.00 16.00-18.00 < 0.75
-
-
 430 Ti  < 0.12 < 1.25 < 0.060 < 0.15 < 1.00 16.00-18.00
-
-
Ti < 0.75
 441  < 0.03 < 1.00 < 0.040 < 0.030 < 1.00 17.50-19.50 < 1.00
-
Ti 0.10 to 0.50